Experimental Evaluation of the Rheological Properties of Veriflex Shape Memory Polymer

Abstract

Shape memory polymers (SMPs) are materials with a great potential for future use in smart materials and structures. When heated from cold state (below the transformation temperature, which can either be the glass transition temperature or the melting temperature of the polymer) to hot state (above the transformation temperature) they undergo transformation which can be compared with martensitic transformation of shape memory alloys. This process induces great changes of the mechanical properties and some shape memory phenomenon can be observed. This study is an experimental evaluation of the mechanical properties of SMP Veriflex under different test conditions. Veriflex was chosen because of its easy accessibility. Furthermore its properties are similar to epoxy resins which make it very suitable for usage in a wide variety of technical applications. Dynamic mechanical analysis (DMA) was used to determine evolution of the viscoelastic properties versus temperature and frequency under cyclic harmonic loading. The glass transition temperature clearly appears in a range from 45\degree C to 60\degree C depending on loading frequency. The glass transition is noticeably marked by an impressive decrease in the storage modulus of about 4 decades. The master curve of Veriflex was created and allows the time-temperature superposition to be constructed for this material. Thermo-mechanical working cycle of SMP with 100% elongation was also experimentally tested. Finally results from all these experimental investigations were used to design a demonstrator showing the possibility of application in engineering and especially for shape control.

Explore related subjects

Keep this discovery

BibTeXRIS

Jan Klesa, Vincent Placet, Emmanuel Foltete, Manuel Collet. 2009-09-16. Experimental Evaluation of the Rheological Properties of Veriflex Shape Memory Polymer. https://doi.org/10.1051/esomat/200904006

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related papers

Slow Dynamics and the Geometry of Jammed Packings

Saddle points in the energy landscape of granular packings dominate the discrete steepest descent dynamics and ultimately determine the path that an out of mechanical equilibrium packing will follow and the resulting stable minimum that it will find. The saddle points that ultimately determine the resulting minima tend to be low-index saddle points. For models with an analytic energy landscape, such as the $p$-spin model, the steepest descent minimization path is affected by higher-index saddle points, which pull the system towards saddle points of decreasing index before arriving at the minima. Here, we examine the steepest descent minimization path of granular packings and compare them to the $p$-spin model. We show that the granular packing steepest descent minimization paths act like their smooth energy landscape counterparts and get attracted by saddle points. The index versus time curves for all models follow a shifted, stretched exponential. We further show that the shape parameter for the granular packings is unchanged when the energy landscape is modified to become analytic (Gaussian potential in a harmonic well) or non-local (Mari-Krzakala-Kurchan). The $p$-spin, on the other hand, has a significantly larger shape parameter. The reason is not due to the dimensionality, packing fraction, nonanalyticity, or the locality of the Hamiltonian of the models. The exact reason for the discrepancy in the shape parameter is \st{still} an unsolved mystery.

cond-mat.soft

A Phase-Field Study of Desiccation Crack Pattern Maturation under Drying-Wetting Cycles

The characteristic intersection angle of the desiccation crack relaxes from near \ang{90} toward \ang{120} under repeated drying--wetting cycles. However, the theoretical understanding of this relaxation is insufficient, especially the modeling of the drying--wetting cycles. Here we introduce a phase-field model of desiccation fracture, extending the model proposed in previous studies by adding crack healing and a scar effect left by past cracks. By repeating drying--wetting cycles in a finite element simulation, we find that the angle distribution develops a growing peak near \ang{120} as the cycle number increases, consistent with experiments. The standard deviation of the intersection angle from \ang{120} relaxes exponentially with a characteristic time of about 2.85 cycles. These results are consistent with experiments, except that the characteristic time is slightly smaller than the experimental value. Crack energy dominates the total energy and also relaxes exponentially with nearly the same characteristic cycle as the angle relaxation. This decay is driven mainly by a shortening of the effective crack length rather than a change in effective fracture toughness.

cond-mat.soft

Kinetics of ferritin crystal formation and melting in acoustically levitated droplets

Understanding protein crystallization pathways is essential for controlling crystallization in structural biology, materials science, and pharmaceutical applications. Classical nucleation theory does not fully capture crystallization processes for several proteins, including ferritin. Here, we combine acoustic levitation with small- and wide-angle X-ray scattering (SAXS and WAXS) to monitor ferritin crystallization in evaporating aqueous polyethylene glycol (PEG) solutions. Acoustic levitation rapidly drives the droplets through a broad range of protein and polymer concentrations, enabling time-resolved measurements of crystallization during evaporation. The scattering data show that ferritin crystals form during evaporation and subsequently lose their crystalline order upon further dehydration. Varying the PEG molecular weight switches between distinct crystallization pathways: one dominated by attractive protein-protein interactions and another dominated by repulsive interactions and excluded-volume effects. Furthermore, we find that lower molecular weight PEG (1000 g/mol) suppresses the dehydration-induced loss of crystalline order observed for higher molecular weight PEG (6000 g/mol), providing a simple strategy for improving protein crystal stability.

cond-mat.soft