The effect of heat treatments and coatings on the outgassing rate of stainless steel chambers

M. A. Mamun·A. A. Elmustafa·M. L. Stutzman·P. A. Adderley·M. Poelker
View original source ↗Read source document ↗Export metadata ↓

Abstract

The outgassing rates of three nominally identical 304L stainless steel vacuum chambers were measured to determine the effect of chamber coatings and heat treatments. One chamber was coated with titanium nitride (TiN) and one with amorphous silicon (a-Si) immediately following fabrication. The last chamber was first tested without any coating, and then coated with a-Si following a series of heat treatments. The outgassing rate of each chamber was measured at room temperatures between 15 and 30 °C following bakes at temperatures between 90 and 400 °C. Measurements for bare steel showed a significant reduction in the outgassing rate by nearly a factor of 20 after a 400 °C heat treatment (3.5x10-12 Torr L s-1 cm-2 prior to heat treatment, reduced to 1.7x10-13 Torr L s-1 cm-2 following heat treatment). The chambers that were coated with a-Si showed minimal change in outgassing rates with heat treatment, though an outgassing rate reduced by heat treatments prior to a-Si coating was successfully preserved throughout a series of bakes. The TiN coated chamber exhibited remarkably low outgassing rates, up to four orders of magnitude lower than the uncoated stainless steel, but the uncertainty in these rates is large due to the sensitivity limitations of the spinning rotor gauge accumulation measurement and the possibility of a small pump speed due to inhomogeneity in the TiN coating. The outgassing results are discussed in terms of diffusion-limited versus recombination-limited processes.

Explore related subjects

physics.ins-detnucl-ex

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

M. A. Mamun, A. A. Elmustafa, M. L. Stutzman, P. A. Adderley, M. Poelker. 2014-01-27. The effect of heat treatments and coatings on the outgassing rate of stainless steel chambers. https://doi.org/10.1116/1.4853795

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related papers

arXiv2026

Kinematic Fitting of electromagnetic calorimeter data - an improved method

Kinematic fitting is widely used in particle physics experiments as a powerful tool to improve experimental resolutions, to suppress background and to provide selection criteria for the identification of specific reactions. Kinematic fitting methods, however, typically assume that the fitted quantities follow Gaussian distributions; an assumption which does not always hold. This is particularly true for energy measurements from electromagnetic calorimeters. This issue can largely be overcome by performing a transformation of the non-Gaussian variables into variables which follow a Gaussian distribution. The new adapted kinematic fitting procedure allows to better account for the non-Gaussian nature of the measured calorimeter energies, at the same time improving the accuracy and robustness of the kinematic fit. This leads to improved pull and confidence-level distributions of the kinematic fit as well as improved invariant mass distributions and signal-to-background ratios in the final event sample.

physics.ins-det↗
arXiv2026

Radiation hardness characterization of SiPM sensors for Low Earth Orbit space missions

This work presents a comprehensive radiation hardness characterization of SiPM devices for space-based applications: FBK NUV-HD-MT and NUV-HD-LowCT (1$\times$1, 3$\times$3, and 6$\times$6~mm$^2$) and Hamamatsu S14160 MPPCs with equivalent active areas. Total Ionizing Dose (TID) tests were performed at the ESA/ESTEC Co-60 facility with a level of dose up to 20~krad in silicon, while displacement damage effects were evaluated using 100~MeV protons with a fluence up to $1.12\times10^{11}$~p/cm$^2$ at the Paul Scherrer Institute. Radiation damage in SiPMs manifests through two main mechanisms: ionizing energy loss and non-ionizing energy loss (NIEL), which increases dark current and dark count rate. In this work, breakdown voltage, dark current, and quenching resistance were systematically measured as functions of accumulated dose and fluence. Gain and dark count rates were indirectly measured from the characterized electrical parameters. Both technologies exhibit remarkable stability of most of the functional parameters across all dose levels, while dark current shows predictable increases significantly more pronounced under proton irradiation due to displacement damage. Based on these results, both FBK and Hamamatsu devices are confirmed suitable for Low Earth Orbit (LEO) mission environment.

physics.ins-det↗
arXiv2026

Characterization of immersed SiPM arrays in liquid scintillator between room temperature and $-30\,^{\circ}\mathrm{C}$

Liquid scintillator detectors instrumented with distributed silicon photomultiplier (SiPM) arrays can be used in compact, topology-sensitive, and low-background experiments, but the temperature dependence of SiPMs immersed directly in the scintillation medium has not been widely characterized. We report the operation of a 125-liter linear-alkylbenzene-based liquid scintillator detector read out by 125 SiPM channels immersed in the active volume, over the range from room temperature to $-30\,^{\circ}\mathrm{C}$. The detector response was measured with cosmic-ray muons, including stopping muons followed by their Michel-electron decay. Cooling from $+15\,^{\circ}\mathrm{C}$ to $-30\,^{\circ}\mathrm{C}$ reduced the SiPM dark-count rate by a factor of 13.5, increased the single-photoelectron response by 49.1%, and increased the cosmic-ray muon light yield by 16.7%. The improved photoelectron separation and baseline stability at low temperature enabled a selection of stopping-muon events, from which the effective muon lifetime was measured to be $1959\pm132\,\mathrm{ns}$, consistent with the value expected for a hydrocarbon scintillator once $μ^{-}$ capture on carbon is taken into account.

physics.ins-det↗