Enhancement of superconductivity on thin film of Sn under high pressure

Abstract

We investigated the pressure effects of a superconductivity on thin films of Sn. Elemental superconductor Sn with a body-centered tetragonal structure, $β$-Sn, exhibits superconductivity below the superconducting transition temperature ($T_{\rm c}=3.72$ K) at ambient pressure. $T_{\rm c}$ of Sn increases with lowering dimension such as in thin film and nanowire growth, or by high-pressure application. For thin films, $T_{\rm c}$ exhibits a slight increase up to approximately 4 K compared to the bulk value, attributable to the crystalline size and lattice disorder. By applying pressure on a bulk Sn, $T_{\rm c}$ initially decreases from 3.72 K as the pressure increases. Further increasing pressure up to 10 GPa, $T_{\rm c}$ increases to 5.3 K with the structural transformation. However, the combination of these effects on thin films of Sn, namely, thin-film growth and pressure effects, remains underexplored. In this study, we combined film-growth and pressure-application techniques to further increase $T_{\rm c}$ using a diamond anvil cell with boron-doped diamond electrodes. The drop of the electrical resistance suggesting the onset of $T_{\rm c}$ on the thin film reached above 6 K in $γ$-Sn phase. Further, the upper critical magnetic field was drastically enhanced. Atomic force microscopy suggests that the refinement of the grain size of the thin film under the non-hydrostatic pressure conditions contributes to stabilizing the higher $T_{\rm c}$ of $γ$-Sn.