arXiv2023

Novel nanoindentation strain rate sweep method for continuously investigating the strain rate sensitivity of materials at the nanoscale

We introduce a new nanoindentation method to continuously measure the hardness while sweeping through orders of magnitudes of strain rates within a single experiment. While nanoindentation already allows the determination of the strain rate sensitivity of materials by means of strain rate jump tests, these are typically limited to few discrete strain rates. With the new method, the strain rate sensitivity can be measured continuously as a function of the strain rate. Applications to fused silica, Zn-22 %Al superplastic alloy, single crystalline aluminum, various nanocrystalline metals and a palladium-based metallic glass are shown. Besides some discrepancy with the reference measurements, the new method seems only affected by the presence of a strong nanoindentation size effect. Provided this indentation size effect is not excessively large and can be corrected for accurately, the method proves robust, with no suggestion that the direction of the strain rate sweep affects the evaluation of the strain rate sensitivity.

physics.app-ph↗

arXiv2022

Structural reorientation and compaction of porous MoS2 coatings during wear testing

Industrial upscaling frequently results in a different coating microstructure than the laboratory prototypes presented in the literature. Here, we investigate the wear behavior of physical vapor deposited (PVD) MoS2 coatings: A dense, nanocrystalline MoS2 coating, and a porous, prismatic-textured MoS2 coating. Transmission electron microscopy (TEM) investigations before and after wear testing evidence a crystallographic reorientation towards a basal texture in both samples. A basal texture is usually desirable due to its low-friction properties. This favorable reorientation is associated to a tribological compaction of the porous specimens. Following running-in, sliding under high contact pressure ultimately leads to a wear rate as small as for an ideal grown bulk MoS2 single crystal grown by chemical vapor deposition (CVD). This suggests that the imperfections of industrial grade MoS2 coatings can be remediated by a suitable pretreatment.

cond-mat.mtrl-sci↗

arXiv2020

Biominerals with Texture Gradients are Functionally Graded Bioceramics Toughened by Stress Delocalization

Biomineralizing organisms are widely noted and extensively studied due to their ability to generate structures exhibiting exceptional crystallographic control. Primarily, it is the organisms, such as sea-urchins or bivalves, that generate nearly single-crystalline biocrystals that have attracted attention. In contrast, biomineralizing organisms with seemingly disordered polycrystalline bio-armor have been left relatively unstudied. However, the crystalline ordering in the black-lipped pearl oyster, Pinctada margaritifera, reveals that biominerals with varying crystal textures are an unrecognized class of functionally graded materials. Changing crystal textures inevitably cause a variation in Young modulus due to the orientation-dependent mechanical properties of crystals. The case of Pinctada margaritifera demonstrates that bioceramics with such crystallographical gradients are toughened by stress delocalization and reduced stress intensity factors, outperforming non-graded counterparts. These findings suggest that a multitude of biominerals, which are perceived as poorly ordered because of their polycrystallinity and changing crystal textures, may be considered as graded materials with hitherto unidentified emergent mechanical properties. The underlying design principle is remarkably simple and applicable to a wide range of crystalline material classes and may thus serve as a blueprint for future bioinspired functional materials.

cond-mat.mtrl-sci↗

arXiv2020

Effect of Cold Sintering Process (CSP) on the Electro-Chemo-Mechanical Properties of Gd-doped Ceria (GDC)

In this report, the effect of the cold sintering process (CSP) on the electro-chemo-mechanical properties of 10 mol% Gd-doped ceria (GDC) is investigated. High purity nanoscale GDC powder is sintered via a cold sintering process (CSP) in pure water followed by post-annealing at 1000 {\deg}C. The resultant CSP ceramics exhibits high relative density (~92%) with an ultrafine grain size of ~100 nm. This sample illustrates comparable electrochemical properties at intermediate/high temperatures and electromechanical properties at room temperature to the sample prepared via conventional firing, i.e. sintering in the air at 1450 {\deg}C. Moreover, a large creep constant as well as a low elastic modulus and hardness are also observed in the CSP sample.

cond-mat.mtrl-sci↗

arXiv2020

The Role of Oxygen Defects on the Electro-Chemo-Mechanical Properties of Highly Defective Gadolinium Doped Ceria

In light of the recent discovery of giant electrostriction in defective fluorites, here we investigate the interplay between mechanical, electrochemical and electromechanical properties of oxygen defective ceria compositions as the effect of Gd-doping at low temperatures. Highly dense polycrystalline ceramics are prepared as micron-size grains with a minimized grain boundary extent. Electrochemical ionic migration reveals that doping controls the configuration of oxygen vacancies in the samples. Unexpectedly, we observe that electromechanical activity depends on oxygen vacancy configuration rather than on its nominal concentration. The primary creep at room temperature indicates a declining viscoelastic trend with increasing oxygen defects.

physics.app-ph↗

arXiv2019

High-pressure synthesis of ultraincompressible hard rhenium nitride pernitride Re$_{2}$(N$_{2}$)N$_{2}$ stable at ambient conditions

Here we report the synthesis of metallic, ultraincompressible (bulk modulus $K_{0}$ = 428(10) GPa) and very hard (nanoindentation hardness 36.7(8) GPa) rhenium (V) nitride pernitride Re$_{2}$(N$_{2}$)N$_{2}$. While the empirical chemical formula of the compound, ReN$_{2}$, is the same as for other known transition metals pernitrides, e.g. IrN$_{2}$, PtN$_{2}$, PdN$_{2}$ and OsN$_{2}$, its crystal chemistry is unique. The known pernitrides of transition metals consist of a metal in the oxidation state +IV and pernitride anions N$_{2}^{4-}$. ReN$_{2}$ contains both pernitride N$_{2}^{4-}$ and discrete N$^{3-}$ anions, which explains its exceptional properties. Moreover, in the original experimental synthesis of Re$_{2}$(N$_{2}$)N$_{2}$ performed in a laser-heated diamond anvil cell via a direct reaction between rhenium and nitrogen at pressures from 40 to 90 GPa we observed that the material was recoverable at ambient conditions. Consequently, we developed a route to scale up its synthesis through a reaction between rhenium and ammonium azide, NH$_{4}$N$_{3}$, in a large-volume press at 33 GPa. Our work resulted not only in a discovery of a novel material with unusual crystal chemistry and a set of properties attractive for potential applications, but also demonstrated a feasibility of surmounting conceptions common in material sciences.

cond-mat.mtrl-sci↗