arXiv2021

Temperature-driven Emergence of Negative Photoconductivity in Semimetal MoTe2 Film Probed with Terahertz Spectroscopy

Layered two-dimensional (2D) materials MoTe2 have been paid special attention due to the rich optoelectronic properties with various phases. The nonequilibrium carrier dynamics as well as its temperature dependence in MoTe2 are of prime importance, as it can shed light on understanding the anomalous optical response and potential applications in far infrared (IR) photodetection. Hereby, we employ time-resolved terahertz (THz) spectroscopy to study the temperature dependent nonequilibrium carrier dynamics in MoTe2 films. After photoexcitation of 1.59 eV, the 1T'-phase MoTe2 at high temperature behaves only THz positive photoconductivity (PPC) with relaxation time of less than 1 ps. In contrast, the Td-phase MoTe2 at low temperature shows ultrafast THz PPC initially followed by emerging THz negative photoconductivity (NPC), and the THz NPC signal relaxes to the equilibrium state in hundreds of ps time scale. Small polaron formation induced by hot carrier has been proposed to be ascribed to the THz NPC in the polar semimetal MoTe2 at low temperature. The polaron formation time after photoexcitation increases slightly with temperature, which is determined to be ~0.4 ps at 5 K and 0.5 ps at 100 K. Our experimental result demonstrates for the first time the dynamical formation of small poalron in MoTe2 Weyl semimetal, this is fundamental importance on the understanding the temperature dependent electron-phonon coupling and quantum phase transition, as well as the designing the MoTe2-based far IR photodetector.

cond-mat.str-el↗

arXiv2020

Observation of Negative THz Photoconductivity in Large Area Type-II Dirac Semimetal PtTe2

As a newly emergent type-II Dirac semimetal, Platinum Telluride (PtTe2) stands out from other 2D noble-transition-metal dichalcogenides for the unique structure and novel physical properties, such as high carrier mobility, strong electron-phonon coupling and tunable bandgap, which make the PtTe2 a good candidate for applications in optoelectronics, valleytronics and far infrared detectors. Although the transport properties of PtTe2 have been studied extensively, the dynamics of the nonequilibrium carriers remain nearly uninvestigated. Herein we employ optical pump-terahertz (THz) probe spectroscopy (OPTP) to systematically study the photocarrier dynamics of PtTe2 thin films with varying pump fluence, temperature, and film thickness. Upon photoexcitation the THz photoconductivity (PC) of 5 nm PtTe2 film shows abrupt increase initially, while the THz PC changes into negative value in a subpicosecond time scale, followed by a prolonged recovery process that lasted hundreds of picoseconds (ps). This unusual THz PC response observed in the 5 nm PtTe2 film was found to be absent in a 2 nm PtTe2 film. We assign the unexpected negative THz PC as the small polaron formation due to the strong electron-Eg-mode phonon coupling, which is further substantiated by pump fluence- and temperature-dependent measurements as well as the Raman spectroscopy. Moreover, our investigations give a subpicosecond time scale of sequential carrier cooling and polaron formation. The present study provides deep insights into the underlying dynamics evolution mechanisms of photocarrier in type-II Dirac semimetal upon photoexcitation, which is fundamental importance for designing PtTe2-based optoelectronic devices.

cond-mat.mtrl-sci↗

arXiv2019

Terahertz emission in the van der Waals magnet CrSiTe3

The van der Waals magnet CrSiTe3 (CST) has captured immense interest because it is capable of retaining the long-range ferromagnetic order even in its monolayer form, thus offering potential use in spintronic devices. Bulk CST crystal has inversion symmetry that is broken on the crystal surface. Here, by employing ultrafast terahertz (THz) emission spectroscopy and time resolved THz spectroscopy, the THz emission of the CST crystal was investigated, which shows a strong THz emission from the crystal surface under femtosecond (fs) pulse excitation at 800 nm. Theoretical analysis based on space symmetry of CST suggests the dominant role of shift current occurring on the surface with a thickness of a few quintuple layers in producing the THz emission, in consistence with the experimental observation that the emitted THz amplitude strongly depends on the azimuthal and pumping polarization angles. The present study offers a new efficient THz emitter as well as a better understanding of the nonlinear optical response of CST. It hopefully will open a window toward the investigation on the nonlinear optical response in the mono-/few-layer van der Waals crystals with low-dimensional magnetism.

physics.optics↗