Presence of Two Maxima in the Isothermal Free-Radical Polymerization Rate of Isobornyl Methacrylate Retarded by Oxygen

Abstract

The kinetics of the free-radical polymerization of isobornyl methacrylate (IBoMA) at 80C, initiated by benzoyl peroxide (BPO), was determined by differential scanning calorimetry (DSC), using sample pans previously sealed in air or in nitrogen. The polymerization was arrested by vitrification at a final conversion close to 0.80. The kinetics in nitrogen could be fitted using initiation and propagation rate constants reported in the literature, a functionality of the termination rate constant controlled by translational diffusion based on the free-volume model, and an efficiency factor for the initiator decomposition that decreased with conversion in the medium-high conversion range. The presence of oxygen led to a significant decrease in the polymerization rate, an effect that was enhanced when decreasing the sample size (increasing the surface-to-volume ratio). The original finding was the presence of two maxima in the isothermal polymerization rate (a double gel effect), a fact that was confirmed by replicating experiences in two different DSC devices and changing the amount of initiator in the formulation. The first maximum in the polymerization rate was explained by the decrease of the diffusion rate of macromolecular radicals to the oxygen-rich boundary, an effect that starts at low conversions. The second maximum was related to the decrease in the solubility/diffusion of oxygen in the reaction medium, a phenomenon that is particularly severe at high conversions.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Ezequiel R. Soule, Julio Borrajo, Roberto J. J. Williams. 2013-11-26. Presence of Two Maxima in the Isothermal Free-Radical Polymerization Rate of Isobornyl Methacrylate Retarded by Oxygen. https://doi.org/10.1021/ma0350314

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related papers

Symmetry-induced magnetic fullerene

Defect-free, charge-neutral, pure-carbon materials are generally viewed as intrinsically non-magnetic. Here we challenge this view by establishing a fundamental principle of symmetry-induced magnetism in pure-carbon fullerene systems through molecular orbital theory. We show that high-order symmetry of fullerene molecules or their crystalline lattices induces degenerate energy levels and hence, quantised magnetic moments at half filling. This mechanism holds for all high-order symmetries. It suggests a plausible intrinsic origin for the previously debated magnetic fullerene. Additionally, recent experimental advances in the synthesis of monolayer fullerene networks provide a feasible platform to implement our prediction on the deep link between symmetry and magnetism in these systems. Our results create new, broad frontiers of quantum magnetism by introducing molecular or crystalline symmetries in any lattice.

cond-mat.mtrl-sci↗

Tritium for Nanoscale Hydrogen Analysis by Atom Probe Tomography

Accurate nanoscale detection of hydrogen is essential for understanding hydrogen-related phenomena in materials, yet conventional tracing with deuterium is often complicated by residual background hydrogen. This study evaluates tritium as a highly resolvable isotopic marker for nanoscale hydrogen analysis in metals using atom probe tomography. Titanium was selected for its ability to incorporate hydrogen isotopes, providing a suitable platform for tritium detection. Time of flight secondary ion mass spectrometry and electron backscatter diffraction were performed prior to tritium charging to characterize the initial composition and microstructure. Atom probe tomography in laser mode before and after tritium charging, at three post-charging time intervals, enables tracking of tritium incorporation over time. Thermal desorption analysis confirmed the presence of tritium and complemented the secondary ion mass spectrometry measurements, highlighting the role of the surface oxide layer in modulating tritium release. While tritium, deuterium, and protium differ in their diffusion and trapping behavior, the distinct mass signal associated with tritium provides a practical advantage for resolving hydrogen at very low concentrations. This work serves as a fundamental benchmarking study for leveraging tritium and atom probe tomography as a combined tool for understanding hydrogen in materials, relevant for interpreting local processes such as hydrogen embrittlement.

cond-mat.mtrl-sci↗

Interfacial melting as a thermodynamic indicator of solid-state synthesizability

Computational materials discovery commonly ranks candidate materials by their thermodynamic stability on the formation energy convex hull, yet many predicted-stable phases resist synthesis. We propose that solid-state synthesizability through interfacial-melt-mediated routes requires an additional thermodynamic condition: the interfacial melt at the target composition must itself remain locally stable against spinodal decomposition. We examine this in the classical Fe--B system, where thermodynamically stable FeB$_4$ has been reported under high-pressure synthesis but not in low-pressure synthesis attempts. Using melt--quench molecular dynamics driven by a fine-tuned machine-learning interatomic potential, we find that, at ambient pressure, the B-rich interfacial melt near the FeB$_4$ composition develops a concave free-energy landscape, signaling a demixing instability that is corroborated by the concentration--concentration structure factor and correlated with low-energy icosahedral and pentagonal-pyramidal boron motifs. In contrast to FeB$_4$, metastable Fe$_3$B and Fe$_{23}$B$_6$ remain synthesizable because their corresponding melts are stable. Applied pressure introduces a convex $PV$ contribution that strongly suppresses this instability, reducing the curvature at the FeB$_4$ composition to within the uncertainty of our fit at 1800~K, consistent with the experimental synthesis boundary. Comparison with CrB$_4$ further shows that weaker melt instability correlates with easier experimental synthesis. Interfacial-melt stability, which atomistic simulations can assess via the low-$k$ concentration--concentration structure factor, is thus proposed as a practical thermodynamic screening descriptor of synthesizability for AI-assisted materials discovery.

cond-mat.mtrl-sci↗