Phase transformations in metastable $β$ Zr15Nb alloy revealed by in-situ methods

Abstract

This study examines the phase transitions occurring during linear heating of the Zr15Nb alloy through a comprehensive, multi-technique methodology comprising in-situ high-energy synchrotron X-ray diffraction (HEXRD), electrical resistance measurements, differential scanning calorimetry (DSC), and thermal expansion analysis, supplemented by ex-situ transmission electron microscopy (TEM). The findings reveal a complex sequence of phase transformations and corresponding structural changes over a broad temperature range (from room temperature up to 800 $°$C). Two distinct body-centered cubic (bcc) $β$ phases - $β_{Zr}$ and $β_{Nb}$ - with closely related lattice parameters are identified. At room temperature, the microstructure is characterized by a mixture of the metastable $β_{Zr}$ + $ω_{ath}$ phase. Upon heating, $β_{Zr}$ progressively decomposes, giving rise to the formation of $β_{Nb}$. TEM observation revealed the cuboidal shape of the $ω_{iso}$ particles resulting from the high lattice misfit between $β$ and $ω$ phase. The $ω$ solvus temperature is determined to be approximately 555 $°$C, as evidenced by in situ HEXRD and abrupt changes in the alloy's thermal and electrical properties. The growth of the $α$ phase occurs after the dissolution of the $ω$ phase, resulting in a pronounced increase in thermal expansion.