Investigation on the temperature dependence of substrate-induced in-plane uniaxial magnetic anisotropy in Ni thin films grown on 128° Y-cut LiNbO3

Abstract

We report the temperature dependence of the substrate-induced magnetic anisotropy in continuous Ni thin films deposited at room temperature using magnetron sputtering on a 128° Y-cut LiNbO3 substrate. Ultrathin films exhibit a pronounced temperature dependence in magnetization, with as-grown films showing isotropic behavior and an unconventional hysteresis branch crossing at relatively low temperatures, whereas no branch crossing is observed in annealed films over the investigated temperature range, indicating suppression of the underlying mechanism. Temperature-dependent magnetization measurements show that post-deposition annealing establishes uniaxial anisotropy with well-defined easy and hard axes, whose strength evolves with temperature due to the nature of residual strain governed by both lattice mismatch and coefficient of thermal expansion (CTE) mismatch between the Ni film and the 128° Y-cut substrate, independent of film thickness for both 5 nm and 100 nm films. The emergence of this anisotropy following annealing indicates enhanced magnetoelastic coupling at the film-substrate interface, as the magnetic response begins to follow the anisotropic strain imposed by lattice mismatch and CTE mismatch.