HVPE Homoepitaxy of $β$-Ga$_2$O$_3$: High-Temperature Growth and Orientation-Dependent Surface Evolution

Abstract

In this work, we systematically investigate homoepitaxial $β$-Ga$_2$O$_3$ growth by halide vapor phase epitaxy (HVPE) on (010), (001), and ($\bar{2}$01) native substrates over a broad growth parameter space, extending the growth temperature as high as 1150 $^\circ$C. The growth kinetics exhibit strong dependence on precursor supply, temperature, reactor pressure, and Ga-source-to-substrate distance. Increasing the HCl flow from 80 to 300 sccm enhances the growth rate by up to seven-fold, while increasing the temperature from 1050 to 1150 $^\circ$C nearly doubles the deposition rate. At 1150 $^\circ$C, atmospheric-pressure growth yields rates more than 2.5 times higher than those at 100 Torr, while reducing the O$_2$ flow to 5 sccm further increases the growth rate to 14.3 $μ$m/h, producing films up to 42.9 $μ$m thick in 3 h. Notably, phase-pure homoepitaxial layers with good crystalline quality are obtained across all three orientations, with low rocking-curve full width at half maximum (FWHM) values of 63.4, 66.6, and 42.8 arcsec for the (010), (001), and ($\bar{2}$01) epilayers, respectively. The surface morphology exhibits a pronounced crystallographic dependence and evolves strongly with the HVPE growth conditions. In particular, the ($\bar{2}$01) surface develops well-defined step-and-terrace morphology with local RMS roughness as low as 0.17 nm. These results extend $β$-Ga$_2$O$_3$ HVPE homoepitaxy into a higher-temperature regime and demonstrate a broad process window for high-rate growth of thick, high-quality epilayers with strongly orientation-dependent surface evolution.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Sourav Sarker, Saleh Ahmed Khan, Ahmed Ibreljic, Pronoy Kanti Das, Anhar Bhuiyan. 2026-10-01. HVPE Homoepitaxy of $β$-Ga$_2$O$_3$: High-Temperature Growth and Orientation-Dependent Surface Evolution. https://arxiv.org/abs/2610.01003

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related papers

Investigation of Fe-Ag and Ag-Fe Interfaces in Ag-57Fe-Ag trilayer Using Nuclear Resonance Scattering under X-ray Standing Wave Conditions

Understanding the interfaces of layered nanostructures is key to optimizing their structural and magnetic properties for the desired functionality. In the present work, the two interfaces of a few nm thick Fe layer in Ag-57Fe-Ag trilayers are studied with a depth resolution of a fraction of a nanometer using x-ray standing waves (XSWs) generated by an underlying [W-Si]x10 multilayer (MLT) at an x-ray incident angle around the Bragg peak of the MLT. Interface selectivity in Ag-57Fe-Ag trilayers was achieved by moving XSW antinodes across the interfaces by optimizing suitable incident angles and performing depth-resolved nuclear resonance scattering (NRS) and X-ray fluorescence (XRF) measurements for magnetic and structural properties. The combined analysis revealed that the rms roughness of 57Fe-on-Ag and Ag-on-57Fe interfaces are not equal. The roughness of the 57Fe-on-Ag interface is 9.7 Angstrom, while that of the Ag-on-57Fe interface is 6.4 Angstrom. 57Fe isotope sensitive NRS revealed that hyperfine field (HFF) at both interfaces of 57Fe-on-Ag and Ag-on-57Fe interfaces are distinct, which is consistent with the difference in interface roughnesses measured as root mean square (RMS) roughness. Thermal annealing induces 57Fe diffusion into the Ag layer, and annealing at 325 C transforms the sample into a paramagnetic state. This behavior is attributed to forming 57Fe nanoparticles within the Ag matrix, exhibiting a paramagnetic nature. These findings provide deep insights into interface properties crucial for developing advanced nanostructures and spintronic devices.

cond-mat.mtrl-sci↗

Strain-induced Dynamic Spin-Phonon Coupling in Epitaxial RuO2 Films

Magnetic order parameters in altermagnets can couple to quantized lattice vibration via both piezomagnetic and magnetoelastic effects, leading to the renormalization of phonon dispersion. Here, we demonstrate photo-induced dynamic frequency modulation of THz phonons excited in anisotropically-strained epitaxial RuO2 thin films using ultrafast coherent phonon spectroscopy and time-resolved magneto-optic Kerr effect measurement. A coherent oscillation of a transverse acoustic phonon appears in the sub-THz range with increasing film thickness above 4 nm due to local dislocation arising from the anisotropic strain relaxation, which hosts large non-zero shear strain. Interestingly, this phonon mode exhibits a time-varying mode hardening below ~ 500 K. Furthermore, an optical phonon oscillation emerges in magnetization dynamics of the photo-induced non-equilibrium state, and it becomes significantly softened near the critical temperature, while there is no observable magneto-optic signal in fully-strain-relaxed films. Such notable dynamic frequency modulations in acoustic and optical phonons offer an opportunity to manipulate phonons in the THz range through the spin-phonon coupling controlled by epitaxial design, which can inspire the new class of altermagnetic applications in the ultrafast quantum opto-spintronics.

cond-mat.mtrl-sci↗

Al$_{1-x}$Hf$_{x}$N Thin Films with Enhanced Piezoelectric Responses for GHz Surface Acoustic Wave Devices

Ternary compounds obtained by alloying wurtzite AlN with transition metals have emerged as promising materials with significantly enhanced piezoelectric characteristics relative to binary AlN. The increased electromechanical coupling in these compounds boosts the performance of high-frequency acoustic devices. So far, progress has largely focused on Al$_{1-x}$Sc$_x$N, which is costly and poorly compatible with complementary metal-oxide-semiconductor (CMOS) technologies. Here, we investigate aluminum hafnium nitride (Al$_{1-x}$Hf$_{x}$N) as a scalable and potentially CMOS-compatible alternative to Al$_{1-x}$Sc$_x$N. Using reactive co-sputtering on both Si and sapphire substrates, we demonstrate wurtzite Al$_{1-x}$Hf$_{x}$N thin films ($x \leq 0.17$) with strong $c$-axis texture and nearly isotropic lattice expansion upon Hf incorporation. X-ray absorption spectroscopy indicates cross-gap hybridization between N 2$p$ and Hf 5$d$ states, which can enhance the Born effective charge and, thereby, the piezoelectric response. Correspondingly, we observe a multifold enhancement in the piezoelectric coefficient, $d_{33}$, relative to AlN, despite increasing structural disorder in Al$_{1-x}$Hf$_{x}$N. Building on this finding, we demonstrate Al$_{1-x}$Hf$_{x}$N GHz surface acoustic wave (SAW) resonators that exhibit enhanced performance, as well as efficient excitation of bulk acoustic waves with low propagation losses. These results establish Al$_{1-x}$Hf$_{x}$N as a promising platform for next-generation high-frequency electromechanical devices, with prospects for further piezoelectric enhancements through improved epitaxy.

cond-mat.mtrl-sci↗